翻訳と辞書 Words near each other ・ Equivalence class (music) ・ Equivalence group ・ Equivalence of categories ・ Equivalence of direct radiation ・ Equivalence of metrics ・ Equivalence partitioning ・ Equivalence point ・ Equivalence principle ・ Equivalence principle (geometric) ・ Equivalence relation ・ Equivalent (chemistry) ・ Equivalent air depth ・ Equivalent airspeed ・ Equivalent annual cost ・ Equivalent average ・ Equivalent carbon content ・ Equivalent circuit ・ Equivalent concentration ・ Equivalent Concrete Performance Concept ・ Equivalent definitions of mathematical structures ・ Equivalent dose ・ Equivalent dumping coefficient ・ Equivalent effective stratospheric chlorine ・ Equivalent impedance transforms ・ Equivalent input ・ Equivalent isotropically radiated power ・ Equivalent Lands ・ Equivalent latitude ・ Equivalent narcotic depth ・ Equivalent National Tertiary Entrance Rank Dictionary Lists mini英和辞書 mini和英辞書 Webster 1913 Latin-English FOLDOC Wikipedia English ウィキペディア

翻訳と辞書　辞書検索 [ 開発暫定版 ] スポンサード リンク Equivalent carbon content ： ウィキペディア英語版 Equivalent carbon content The equivalent carbon content concept is used on ferrous materials, typically steel and cast iron, to determine various properties of the alloy when more than just carbon is used as an alloyant, which is typical. The idea is to convert the percentage of alloying elements other than carbon to the equivalent carbon percentage, because the iron-carbon phases are better understood than other iron-alloy phases. Most commonly this concept is used in welding, but it is also used when heat treating and casting cast iron. ==Steel== In welding, equivalent carbon content (CE) is used to understand how the different alloying elements affect hardness of the steel being welded. This is then directly related to hydrogen-induced cold cracking, which is the most common weld defect for steel, thus it is most commonly used to determine weldability. Higher concentrations of carbon and other alloying elements such as manganese, chromium, silicon, molybdenum, vanadium, copper, and nickel tend to increase hardness and decrease weldability. Each of these elements tends to influence the hardness and weldability of the steel to different magnitudes, however, making a method of comparison necessary to judge the difference in hardness between two alloys made of different alloying elements.〔.〕 There are two commonly used formulas for calculating the equivalent carbon content. One is from the American Welding Society (AWS) and recommended for structural steels and the other is the formula based on the International Institute of Welding (IIW).〔.〕 The AWS states that for an equivalent carbon content above 0.40% there is a potential for cracking in the heat-affected zone (HAZ) on flame cut edges and welds. However, structural engineering standards rarely use CE, but rather limit the maximum percentage of certain alloying elements. This practice started before the CE concept existed, so just continues to be used. This has led to issues because certain high strength steels are now being used that have a CE higher than 0.50% that have brittle failures.〔 :$CE\; =\; \backslash \%C\; +\; \backslash left(\backslash frac\; \backslash right)\; +\; \backslash left(\backslash frac\; \backslash right)\; +\; \backslash left(\backslash frac\; \backslash right)$ The other and most popular formula is the Dearden and O'Neill formula, which was adopted by IIW in 1967. This formula has been found suitable for predicting hardenability in a large range of commonly used plain carbon and carbon-manganese steels, but not to microalloyed high-strength low-alloy steels or low-alloy Cr-Mo steels. The formula is defined as follows:〔 :$CE\; =\; \backslash \%C\; +\; \backslash frac\; +\; \backslash left(\backslash frac\; \backslash right)\; +\; \backslash left(\backslash frac\; \backslash right)$ For this equation the weldability based on a range of CE values can be defined as follows:〔 The Japanese Welding Engineering Society adopted the critical metal parameter (Pcm) for weld cracking, which was based on the work from Ito and Bessyo, is:〔 :$Pcm\; =\; \backslash \%C\; +\; \backslash frac\; +\; \backslash frac\; +\; \backslash frac\; +\; \backslash frac+\backslash frac+5B$ If some of the values are not available, the following formula is sometimes used: :$CE\; =\; \backslash \%C\; +\; \backslash frac\; +\; 0.05$ The carbon equivalent is a measure of the tendency of the weld to form martensite on cooling and to suffer brittle fracture. When the carbon equivalent is between 0.40 and 0.60 weld preheat may be necessary. When the carbon equivalent is above 0.60, preheat is necessary, postheat may be necessary. The following carbon equivalent formula is used to determine if a spot weld will fail in high-strength low-alloy steel due to excessive hardenability:〔 :$CE\; =\; \backslash \%C\; +\; \backslash frac\; +\; \backslash left(\backslash frac\; \backslash right)\; +\; \backslash frac\; +\; \backslash frac\; +\; \backslash frac\; +\; \backslash frac\; +\; \backslash frac$ Where UTS is the ultimate tensile strength in ksi and h is the strip thickness in inches. A CE value of 0.3 or less is considered safe.〔 A special carbon equivalent was developed by Yorioka, which could determine the critical time in seconds ''Δt8-5'' for the formation of martensitic in the Heat Affected Zone (HAZ) in low-carbon alloy steels. The equation is given as: $CE$ * = \%C * + \frac + \frac + \frac + \frac + \frac where: ::$\backslash \%C$ * = 5\%C \mbox \%C \le 0.30\% ::$\backslash \%C$ * = \%C/6 \mbox \%C \ge 0.30\% Then the critical time length in seconds ''Δt8-5'' can be determined as follows: ::$\backslash log\_\; \backslash Delta\; t\_\; =\; 2.69\; CE$ * 抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』 ■ウィキペディアで「Equivalent carbon content」の詳細全文を読む スポンサード リンク 翻訳と辞書 : 翻訳のためのインターネットリソース Copyright(C) kotoba.ne.jp 1997-2016. All Rights Reserved.